The compound with high proportion of phosphorus will result in a more active and fluid alloy which can flow over a larger area. The alloy usually has a smaller melting range and best used on filler joint. Higher proportion of silver alloy will result in a fluid which is easier to be controlled by operators. The silver alloy with less phosphorus may have a melting range which suitable for filling gaps. Generally, higher silver content alloy can bear hotter or longer heating cycle. Moreover, the resulted joints have better ductility.
MAIN USE: Refrigerator, air conditioner, heating exchanger, electric machine, brass alloy and others.
Silver Brazing Alloys
|
Chemical Composition
|
AWS/JIS
|
Reference Data
|
Density kg/cm3
|
Application
|
Ag
|
Cu
|
P
|
Other elements
|
Spec Class
|
Solidus
oC
|
Liquidus oC
|
CI-P007
|
-
|
93
|
7
|
<0.2
|
BCuP-2
|
705
|
805
|
8.05
|
0% of silver, the alloy fluid can flow along the joint border which can reduce the alloy spread the surface.
|
CI-P008
|
-
|
92
|
8
|
<0.2
|
|
700
|
800
|
8.0
|
0% of silver, rapid and extensive fluidity. The fluid may spread the surface which is not easy to be controlled by operator
|
CI-001
|
1
|
92
|
7
|
<0.2
|
|
640
|
800
|
8.1
|
Instead of CI-002 for saving cost
|
CI-002
|
2
|
91
|
7
|
<0.2
|
BCuP-6
|
645
|
740
|
8.1
|
2% of silver spread extensively; Best used on filler joint.
|
CI-003
|
3
|
91
|
6
|
<0.2
|
|
630
|
785
|
8.2
|
Instead of CI-005 for saving cost
|
CI-005
|
5
|
89
|
6
|
<0.2
|
BCuP-3
|
640
|
805
|
8.2
|
5% of silver, used as a temperature inhibitor.
|
CI-006
|
6
|
86.8
|
7.2
|
<0.2
|
BCuP-4
|
645
|
725
|
8.2
|
Good fluidity & similar to CI-005.
|
CI-101
|
10
|
84.5
|
5.5
|
<0.2
|
|
|
|
|
Less silver content than Cl-151, economical product.
|
CI-151
|
15
|
80
|
5
|
<0.2
|
BCuP-5
|
645
|
770
|
8.4
|
Lower melting range. Can be applied to various industries.
|
CI-P181
|
18
|
74.8
|
7.2
|
<0.2
|
|
645
|
670
|
8.6
|
Lowest melting range & best fluidity among the copper-phosphorus series.
|
CI-P201
|
20
|
74
|
6
|
<0.2
|
|
630
|
660
|
8.7
|
Better for large quantity of brazing than others
|
CI-Sn7
|
-
|
86.25
|
6.75
|
Sn 7
|
|
650
|
700
|
8.0
|
Can be used to instead of CI-002 or CI-005. Good fluidity.
|
|